Garlock 5500

所属分类：

非石棉垫片

电话：+86 15202135592

电子邮件：shxflzh@Hotmail.com

询价

产品描述

商品名称: Garlock 5500

MATERIAL PROPERTIES

Color:	Gray
Composition:	Inorganic fibers with a nitrile binder
Fluid Services1 :	Saturated steam3, most refrigerants, water, oils, gasoline and aliphatic
	hydrocarbons
Temperature2 , °F (°C)
Minimum:	-100 (-73)
Continuous Max:	+550 (+288)
Maximum:	+800 (+427)
Pressure2 , Maximum, psig (bar):	1200 (83)
P x T (max.)2 , psig x °F (bar x °C)
1/32 and 1/16":	400,000 (14,000)
1/8":	275,000 (9,600)
Meets Specification:	ABS (American Bureau of Shipping) and Fire Safe

PHYSICAL PROPERTIES*

ASTM F36	Compressibility, range, %:	7-17
ASTM F36	Recovery, %:	50
ASTM F38	Creep Relaxation, %:	15
ASTM F152	Tensile, Across Grain, psi (N/mm2):	1500 (10)
ASTM F1315	Density, lbs./ft.3(grams/cm3):	110 (1.76)
ASTM F433	Thermal Conductivity (K), W/m°K (Btu.·in./hr.·ft.2·°F):	0.43-0.53 (3.00-3.65)
ASTM D149	Dielectric Properties, range, volts/mil.
	Sample conditioning	1/16"		1/8"
	3 hours at 250°F:	284		245
	96 hours at 100% Relative Humidity	-		-
ASTM F586	Design Factors	1/16"		1/8"
	"m" factor:	6.6		6.6
	"y" factor, psi (N/mm2):	2600 (17.9)		3300 (22.8)
ROTT	Gasket Constants, 1/16":	Gb=1,247	a=0.249	Gs=11.0
ASTM F104	Line Call Out:	F712103A9B4E23K7L501M4(4)

SEALING CHARACTERISTICS

	ASTM F37B Fuel A	ASTM F37B Nitrogen	DIN 3535- 4 Gas Permeability
Gasket Load, psi (N/mm2):	500 (3.5)	3000 (20.7)	4640 (32)
Internal Pressure, psig (bar):	9.8 (0.7)	30 (2)	580 (40)
Leakage	0.2 ml/hr.	1.0 ml/hr.	0.05 cc/min

IMMERSION PROPERTIES*- ASTM F146 Fluid Resistance after Five Hour

	ASTM #1 Oil 300°F (150°C)	ASTM IRM #903 300°F (150°C)	ASTM Fuel A 70-85°F (20-30°C)	ASTM Fuel B 70-85°F (20-30°C)
Thickness Increase, (%)	0-10	0-15	0-10	0-15
Weight Increase, (%)	<15	-	<10	<15
Tensile Loss, (%)	-	<40	-	-

Notes：

This is a general guide and should not be the sole means of selecting or rejecting this material. ASTM test results in accordance with ASTM F-104; properties based on 1/32" (0.8mm) sheet thickness unless otherwise mentioned.
* Values do not constitute specification Limits
1.See Garlock chemical resistance guide.
2.Based on ANSI RF flanges at our preferred torque. When approaching maximum pressure, continuous operating temperature, minimum temperature or 50% of maximum PxT, consult Garlock Applications Engineering. Minimum temperature rating is conservative.
3.Minimum recommended assembly stress = 4,800psi. Preferred assembly stress = 6,000-10,000psi. Gasket thickness of 1/16" strongly preferred. Retorque the bolts/studs prior to pressurizing the assembly. For saturated steam above 150psig or superheated steam, consult Garlock Engineering
4.A9: Leakage in Fuel A (Isooctane), Gasket Load = 500psi (3.5N/mm2), Pressure = 9.8psig (0.7bar): Typical = 0.2ml/hr, Max = 1.0ml/hr. A9: Leakage in Nitrogen, Gasket Load = 3,000psi (20.7N/mm2), Pressure = 30psig (2bar): Typical = 0.5ml/hr, Max = 1.5ml/hr.